000000343 245__ $$aAcoustic emission from BiSrCaCuO superconducting samples
000000343 260__ $$c2002-08-01
000000343 300__ $$a4p
000000343 500__ $$aPhysica C, Vol: 372-376, Part 1, August, 2002, pp. 312-315
000000343 520__ $$aThe aim of the paper was to show if the acoustic emission (AE) signals from BiSrCaCuO ceramic superconductors appear during normal state–superconductivity transition. These AE signals were previously observed from YBaCuO-type superconducting materials. The BiSrCaCuO samples were prepared and characterised. The resistance–temperature and current–voltage characteristics of these samples were measured. The critical temperature and critical current density were estimated. AE was measured from samples with and without current flow. The AE signals during sample temperature rise were observed at temperature near the critical value.
000000343 6531_ $$aacoustic emission
000000343 6531_ $$aBiSrCaCuO
000000343 6531_ $$asuperconductor
000000343 700__ $$aWozny, L$$uWroclaw University of Technology
000000343 8560_ $$fleon99@pwr.wroc.pl
000000343 8564_ $$uhttp://zet10.ipee.pwr.wroc.pl/record/343/files/$$zAccess to Fulltext
000000343 909CO $$ooai:zet10.pwr.wroc.pl:343$$pglobal
000000343 980__ $$aARTICLE